C276 / N10276 Inconel Pipe Welding For Waste Treatment NiMo16Cr15W Multifunction

din 17744, din 17750 / din 17751 Alloy C276 / N10276 / 2.4819 / NiMo16Cr15W Hastelloy Alloy pipe

We zheheng steel produce din 17744 c276 pipe, UNS N10276 alloy c276 pipe ,DIN W. Nr. 2.4819 c276 alloy pipe ,din 17750 Hastelloy c276 pipe / din 17751 Alloy C276 alloy pipe / N10276 alloy pipe / 2.4819 alloy c276 pipe  / NiMo16Cr15W Hastelloy Alloy pipe and supply din   Hastelloy Alloy pipe Nickel Alloy Pipe Hastelloy Alloy pipe
We warmly welcome friends at home and abroad to contact us for cooperation based on mutual benefits for a bright and successful future.

Products description:
Equivalent designations

UNS N10276
DIN W. Nr. 2.4819

Alloy 276Chemical composition:

Alloy 276 Physical properties

Features: Hastelloy C-276 pipe has excellent resistance to localized corrosion, stress corrosion cracking, and to both oxidizing and reducing media, thus making it suitable for a wide variety of chemical process environments, including ferric and cupric chlorides, hot contaminated media (organic and inorganic), formic and acetic acids, seawater and brine solutions. It is one of the few materials that withstands the corrosive effects of wet chlorine gas, hypochlorite and chlorine dioxide.

Applications: Chemical processing, waste treatment, pollution control, pulp and paper production, and marine engineering.

Note: Hastelloy is a registered trademark of Haynes International, Inc.

Referenced Documents ASTM Standards:
B751 Specification for General Requirements for Nickel and Nickel Alloy Welded Tube E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS) General Requirements
Material furnished in accordance with this specification shall conform to the applicable requirements of the current edition of Specification B751 unless otherwise provided herein

Materials and Manufacture
1 The tubes shall be made from flat-rolled alloy by an automatic welding process with no addition of filler metal.
2 Subsequent to welding and prior to final heat treatment,Class II and Class III tubes shall be cold worked either in both weld and base metal or in weld metal only. The method and amount of cold working may be specified by the purchaser.When cold drawn, the purchaser may specify the minimum amount of reduction in cross-sectional area or wall thickness,or both.
3 All tubes shall be furnished in the solution annealed and descaled condition. When atmosphere control is used, descaling is not necessary..

product show :