Product Details
Place of Origin: Wenzhou,China
Brand Name: Zheheng
Certification: ISO9001
Model Number: 440A/B/C
Payment & Shipping Terms
Minimum Order Quantity: MOQ500kg
Packaging Details: In wooded cases or pallets,or as for clients requirement
Delivery Time: 7-15 working days after receiving payment
Payment Terms: L/C, D/P, T/T, Western Union
Supply Ability: 1000 Ton/Tons per Month
Port: |
Ningbo |
OD: |
Φ6--630mm |
Section Shape: |
Round |
Package: |
Seaworthy Standard Package |
Price Terms: |
FOB,CIF,CFR,EXW |
Length: |
1-12m |
Technique: |
Hot Rolled/Cold Rolled |
Wall Thickness: |
1-40mm |
Grade: |
400 Series |
Other Grade: |
UNS S44004/X105CrMo17/1.4125 |
Port: |
Ningbo |
OD: |
Φ6--630mm |
Section Shape: |
Round |
Package: |
Seaworthy Standard Package |
Price Terms: |
FOB,CIF,CFR,EXW |
Length: |
1-12m |
Technique: |
Hot Rolled/Cold Rolled |
Wall Thickness: |
1-40mm |
Grade: |
400 Series |
Other Grade: |
UNS S44004/X105CrMo17/1.4125 |
Overview
Stainless 440C is a high-carbon martensitic stainless steel. As a martensitic stainless steel, 440C is magnetic and can be hardened by heat treatment. The high carbon content in 440C provides high hardness and strength. Despite this carbon content, the chromium content is sufficient to retain its stainless characteristics. Martensitic steels are commonly used in applications where high strength and moderate corrosion resistance is required.
Application
Valve Seats
Surgical Instruments
Bearings
Bushings
Nozzles
Structural Aircraft Parts
440 Stainless Pipe Chemical Composition
| 440 Stainless Steel Chemical Composition, % | |||||||||
| ASTM | Steel | AISI (UNS) | C | Si (≤) | Mn (≤) | P (≤) | S (≤) | Cr | Mo (≤) |
| ASTM A276/A276M | 440 Steel | 440A (S44002) | 0.60-0.75 | 1 | 1 | 0.04 | 0.03 | 16.0-18.0 | 0.75 |
| 440B (S44003) | 0.75-0.95 | 1 | 1 | 0.04 | 0.03 | 16.0-18.0 | 0.75 | ||
| 440C (S44004) | 0.95-1.20 | 1 | 1 | 0.04 | 0.03 | 16.0-18.0 | 0.75 | ||
Physical Properties
| SS440 Physical Properties | |
| Density (g/cm3) | 7.8 |
| Melting point (℃) | 1370-1480 |
| Specific heat capacity, J/(Kg·K) | 460 (0-100 ℃) |
| Electrical resistivity (μΩ·m) | 0.6 (20 ℃) |
| Elastic modulus (GPa) | 200 |
| Thermal conductivity (W/m·K) | 24.2 (100 ℃) |
| Coefficient of thermal expansion | 10.2 (0-100 ℃) |
Mechanical Properties Stainless Steel 440
| Mechanical Properties | |||||
| Grade (UNS) | Tensile Strength (MPa) ≥ | Yield Strength, 0.2%, ≥ (MPa) | Elongation in 50 mm (%) ≥ | Reduction in area (%) | Hardness |
| 440A (S44002) | 725 | 415 | 20 | 95 HRB | |
| 1790 | 1650 | 5 | 20 | 51 HRC | |
| ≤ 965 | |||||
| 440B (S44003) | 740 | 425 | 18 | 96 HRB | |
| 1930 | 1860 | 3 | 15 | 55 HRC | |
| ≤ 965 | |||||
| 440C (S44004) | 760 | 450 | 14 | 97 HRB | |
| 1970 | 1900 | 2 | 10 | 57 HRC | |
| ≤ 965 | |||||
SS440 Heat Resistance
AISI 440 has good oxidation resistance in intermittent use below 815 °C and continuous use up to 760 °C in air.
Heat Treatment of SS440
SS440 heat treatment including annealing, quenching, tempering and stress relieving, etc.
Subcritical annealing temperature range: 675-760 ℃ (1250-1400 ℉)
Full annealing: insulation from 845-900 °C (1550-1650 ℉) to completely soaking, then furnace cooling to 790 °C, continue cooling to 595 ° C at a cooling rate of 15-25 °C/h, then air cool to room temperature.
Isothermal Annealing: heat treat to 845-900 °C, kept at 690 °C for 4 hours.
SS440 Quenching
Heat to 1010-1065 °C and quench in air or oil. To ensure maximum dimensional stability, cold treatment should be performed immediately after cooling to room temperature